Ahmad Khairi, Muntaz Hana and Mhd Noor, Ervina Efzan and Ubaidillah, Ubaidillah and Abdul Aziz, Siti Aishah and Mazlan, Saiful Amri and Ahmad Tarmizi, Siti Maisarah and Nordin, Nur Azmah (2022) Enhancement of Magneto-Induced Modulus by the Combination of Filler and Plasticizer Additives-Based Magnetorheological Elastomer. Materials, 15 (18). p. 6396. ISSN 1996-1944
Text
materials-15-06396.pdf - Published Version Restricted to Repository staff only Download (2MB) |
Abstract
Filler additive is used to provide superior bonding in rubber matrix to enhance the storage modulus of magnetorheological elastomer (MRE). However, the magneto-induced modulus is reduced as the initial storage modulus increases. Therefore, this paper aims to increase the magneto-induced modulus and maintain the initial storage modulus by combining filler and plasticizer additives. Both types of additives have different functions, where cobalt ferrite (CoFe2O4) is capable of enhancing the maximum storage modulus and silicone oil (SO) reduces the initial storage modulus. Thus, four MRE samples have been fabricated using (a) no additive, (b) CoFe2O4, (c) SO, and (d) a combination of CoFe2O4 and SO. The sample’s hardness and magnetic properties were investigated via Durometer Shore A and Vibrating Sample Magnetometer (VSM), respectively. Furthermore, the rheological properties of MRE samples in terms of storage modulus were investigated upon the frequency and magnetic field sweep using a rheometer. The results demonstrated that the storage modulus of the MRE samples has increased with increasing the oscillation frequency from 0.1 to 50 Hz. Interestingly, the combination of additives has produced the largest value of magneto-induced modulus of 0.90 MPa as compared to other samples. Furthermore, their initial storage modulus was in between samples with SO (lowest) and without additive (highest). Therefore, fundamental knowledge in adding the combination of additives can offer solutions for a wide range of stiffness in MR device applications such as vibration and noise control devices, sensing devices, and actuators.
Item Type: | Article |
---|---|
Uncontrolled Keywords: | Magnetorheological elastomer, magneto-induced modulus, CoFe2O4, plasticizer, solid additive |
Subjects: | T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK7800-8360 Electronics > TK7871 Electronics--Materials |
Divisions: | Faculty of Engineering and Technology (FET) |
Depositing User: | Ms Nurul Iqtiani Ahmad |
Date Deposited: | 31 Oct 2022 07:38 |
Last Modified: | 31 Oct 2022 07:38 |
URII: | http://shdl.mmu.edu.my/id/eprint/10585 |
Downloads
Downloads per month over past year
Edit (login required) |