Teo, Guo Sheng and Liew, Kia Wai and Kok, Chee Kuang (2022) A Study on Friction Stir Processing Parameters of Recycled AA 6063/TiO2 Surface Composites for Better Tribological Performance. Metals, 12 (6). p. 973. ISSN 2075-4701
Text
43.pdf - Published Version Restricted to Repository staff only Download (14MB) |
Abstract
This work aims to determine and select the suitable friction stir processing parameters for recycled aluminum alloy 6063 surface composites reinforced with titanium dioxide for better tribological performance. A medium range of processing parameters (1200–2000 rpm, 25–45 mm/min) were used to compare with a unique relatively high rotational speed of 2442 rpm and feed rate of 50 mm/min for the sample fabrication. The surface composites’ microhardness was measured and the friction and wear performance were tested using the pin-on-disc tribo-tester under starved lubrication conditions. The results show that surface composites produced at a high rotational speed of 2442 rpm and feed rate of 50 mm/min improved 45% in surface microhardness and reduced the friction coefficient and wear rate by 39% and 73%, respectively, compared to the substrate material.
Item Type: | Article |
---|---|
Uncontrolled Keywords: | Friction stir processing (FSP), FSP parameters selection, FSPed recycled |
Subjects: | T Technology > TA Engineering (General). Civil engineering (General) > TA630-695 Structural engineering (General) |
Divisions: | Faculty of Engineering and Technology (FET) |
Depositing User: | Ms Nurul Iqtiani Ahmad |
Date Deposited: | 29 Jul 2022 01:43 |
Last Modified: | 29 Jul 2022 01:43 |
URII: | http://shdl.mmu.edu.my/id/eprint/10244 |
Downloads
Downloads per month over past year
Edit (login required) |