Pitting corrosion induced on high-strength high carbon steel wire in high alkaline deaerated chloride electrolyte

Citation

Lee, Siaw Foon and García, Jose Fullea and Yap, Seong Shan and Hui, David (2022) Pitting corrosion induced on high-strength high carbon steel wire in high alkaline deaerated chloride electrolyte. Nanotechnology Reviews, 11 (1). pp. 973-986. ISSN 2191-9097

[img] Text
Pitting corrosion induced on.pdf
Restricted to Repository staff only

Download (9MB)

Abstract

Electrochemical response causing pitting corrosion of high-strength high carbon steel wire in deaerated electrolyte at pH 13.4 due to different chloride ion (Cl−) concentrations was investigated using open circuit potential, cyclic potentiodynamic polarization, and anodic potentiostatic application (APA) within the passive zone. Results showed that the higher the Cl− concentration, the more negative the corrosion potential becomes. In the high alkaline pH 13.4 without the presence of free oxygen gas the Cl− concentration could reach up to 1 M not showing pitting potential. An inverse relationship between anodic potentials (APs) and Cl− concentrations was found and the rate of corrosion within passive period was almost a constant, not influenced by the Cl− concentrations. Faraday´s law failed to predict the mass loss when active pitting corrosion occurred. Green rust and hydrogen gas were observed during active pitting corrosion under APA. Pitting corrosion mechanism in the deaerated high alkaline electrolyte was then proposed. This work deduces that in the deaerated electrolyte at pH 13.4 with the presence of Cl−, it is essential to apply the APs within the safety margin on the high-strength high carbon steel wire to avoid active pitting corrosion and hydrogen embrittlement.

Item Type: Article
Uncontrolled Keywords: Pitting corrosion, anodic potential, deaerated high alkaline
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA401-492 Materials of engineering and construction. Mechanics of materials
Divisions: Faculty of Engineering (FOE)
Depositing User: Ms Nurul Iqtiani Ahmad
Date Deposited: 06 Apr 2022 02:08
Last Modified: 06 Apr 2022 02:08
URII: http://shdl.mmu.edu.my/id/eprint/10050